WIDE RANGE OF MATERIALS
WIDE RANGE OF MATERIALS
Verified materials made in Europe
High quality materials provide the highest quality products.
ASA
Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 100 °C
Density: 1.07 g/cm3
Tensile strength: 47 MPa
Flexural strength: 75 MPa
ABS+
Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 100 °C
Density: 1.04 g/cm3
Tensile strength: 24,2 MPa
Flexural strength: 42,4 MPa
PET
Strength: HIGH
Flexibility: LOW
Durability: HIGH
Temperature resistance: 100 °C
Density: 1.23 g/cm3
Tensile strength: 61 MPa
Flexural strength: 82 MPa
PET-G
Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 85 °C
Density: 1.29 g/cm3
Tensile strength: 20 MPa
Flexural strength: 68 MPa
NYLON
Strength: HIGH
Flexibility: HIGH
Durability: HIGH
Temperature resistance: 120 °C
Density: 1.13 g/cm3
Tensile strength: 48 MPa
Flexural strength: 97 MPa
PC
Strength: VERY HIGH
Flexibility: MEDIUM
Durability: VERY HIGH
Temperature resistance: 120 °C
Density: 1.18 g/cm3
Tensile strength: 68 MPa
Flexural strength: 100 MPa
PET-CARBON FIBER
Strength: VERY HIGH
Flexibility: LOW
Durability: VERY HIGH
Temperature resistance: 125 °C
Density: 1.4 g/cm3
Tensile strength: 80 MPa
Flexural strength: 130 MPa
PAHT-CARBON FIBER
Strength: VERY HIGH
Flexibility: LOW
Durability: VERY HIGH
Temperature resistance: 160 °C
Density: 1.24 g/cm3
Tensile strength: 130 MPa
Flexural strength: 160 MPa
HIPS
Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 90 °C
Density: 1.08 g/cm3
Tensile strength: 34 MPa
Flexural strength: 43 MPa
WOOD
Strength: HIGH
Flexibility: MEDIUM
Durability: MEDIUM
Temperature resistance: 60 °C
Density: 1.19 g/cm3
Tensile strength: 47 MPa
Flexural strength: 52 MPa
FLEX
Strength: MEDIUM
Flexibility: VERY HIGH
Durability: VERY HIGH
Temperature resistance: 80 °C
Density: 1.17 g/cm3
Tensile strength: 45 MPa
Tear strength: 120 N/mm
SILK
Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 60 °C
Density: 1.24 g/cm3
Tensile strength: 59 MPa
Flexural strength: 73 MPa
MARBLE
Strength: HIGH
Flexibility: LOW
Durability: HIGH
Temperature resistance: 60 °C
Density: 1.21 g/cm3
Tensile strength: 49 MPa
Flexural strength: 57 MPa
IMPACT RESISTANT PLA
Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 60 °C
Density: 1.27 g/cm3
Tensile strength: 41 MPa
Flexural strength: 52 MPa
PLA-GLOW IN THE DARK
Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 60 °C
Density: 1.20 g/cm3
Tensile strength: 40 MPa
Flexural strength: 49 MPa
Materials listed above, are just for easier understanding of mechanical properties between different types of plastics. Mechanical properties of 3D printed part depends on its design and shape.