WIDE RANGE OF MATERIALS

WIDE RANGE OF MATERIALS

Verified materials made in Europe

High quality materials provide the highest quality products.

ASA

Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 100 °C
Density: 1.07 g/cm3
Tensile strength: 47 MPa
Flexural strength: 75 MPa

ABS+

Strength: HIGH 
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 100 °C
Density: 1.04 g/cm3 
Tensile strength: 24,2 MPa
Flexural strength: 42,4 MPa

PET

Strength: HIGH
Flexibility: LOW
Durability: HIGH
Temperature resistance: 100 °C
Density: 1.23 g/cm3
Tensile strength: 61 MPa
Flexural strength: 82 MPa

PET-G

Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 85 °C
Density: 1.29 g/cm3
Tensile strength: 20 MPa
Flexural strength: 68 MPa

NYLON

Strength: HIGH
Flexibility: HIGH
Durability: HIGH
Temperature resistance: 120 °C
Density: 1.13 g/cm3
Tensile strength: 48 MPa
Flexural strength: 97 MPa

PC

Strength: VERY HIGH
Flexibility: MEDIUM
Durability: VERY HIGH
Temperature resistance: 120 °C
Density: 1.18 g/cm3
Tensile strength: 68 MPa
Flexural strength: 100 MPa

PET-CARBON FIBER

Strength: VERY HIGH
Flexibility: LOW
Durability: VERY HIGH
Temperature resistance: 125 °C
Density: 1.4 g/cm3
Tensile strength: 80 MPa
Flexural strength: 130 MPa

PAHT-CARBON FIBER

Strength: VERY HIGH
Flexibility: LOW
Durability: VERY HIGH
Temperature resistance: 160 °C
Density: 1.24 g/cm3
Tensile strength: 130 MPa
Flexural strength: 160 MPa

HIPS

Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 90 °C
Density: 1.08 g/cm3
Tensile strength: 34 MPa
Flexural strength: 43 MPa

WOOD

Strength: HIGH
Flexibility: MEDIUM
Durability: MEDIUM
Temperature resistance: 60 °C
Density: 1.19 g/cm3
Tensile strength: 47 MPa
Flexural strength: 52 MPa 

FLEX

Strength: MEDIUM
Flexibility: VERY HIGH
Durability: VERY HIGH
Temperature resistance: 80 °C
Density: 1.17 g/cm3
Tensile strength: 45 MPa
Tear strength: 120 N/mm

SILK

Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 60 °C
Density: 1.24 g/cm3
Tensile strength: 59 MPa
Flexural strength: 73 MPa

MARBLE

Strength: HIGH
Flexibility: LOW
Durability: HIGH
Temperature resistance: 60 °C
Density: 1.21 g/cm3
Tensile strength: 49 MPa
Flexural strength: 57 MPa

IMPACT RESISTANT PLA

Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 60 °C
Density: 1.27 g/cm3
Tensile strength: 41 MPa
Flexural strength: 52 MPa

PLA-GLOW IN THE DARK

Strength: HIGH
Flexibility: MEDIUM
Durability: HIGH
Temperature resistance: 60 °C
Density: 1.20 g/cm3
Tensile strength: 40 MPa
Flexural strength: 49 MPa

Materials listed above, are just for easier understanding of mechanical properties between different types of plastics. Mechanical properties of 3D printed part depends on its design and shape.